SICHUAN FOREVER RADIATION TECHNOLOGY CO.,LTD
$23≥50Roll
| Payment Type: | T/T |
| Incoterm: | FOB,CFR,EXW,CIF,FCA |
| Min. Order: | 50 Roll |
| Transportation: | Ocean,Land,Air,Express |
| Port: | Shanghai,Qingdao,Shenzhen |
Share:
Model No.: VET
Brand: Forever
Origin: China
Certification: ISO 9001
Place Of Origin: China
Classification: Other Adhesives
Application Field: Construction
Width: 50mm, 100 mm, 150 mm, 200 mm and 300 mm
Length: 10m,20 m
Standard: ISO 21809-3 FJC 13A
Competior's Brand: Stopaq, Viscotaq
Warranty Period: 24 months
| Selling Units | : | Roll |
| Package Type | : | Paperboard,Tape Core and Box |
| Picture Example | : |
|
The file is encrypted. Please fill in the following information to continue accessing it
Why use Visco Ealstic Body Adhesive Tape ?
Saves time, surface preparation no need blasting and preheating, without applying Epoxy Primer
Super bonding to Steel, and any coating material include PE, PP, FBE and AE
Superior cathodic disbondment offers the optimum barrier long term protection against corrosion.
Self-healing ability when slightly damaged due to plastic-elastic properties
No flowing and dripping on maximum operation temperature
Impermeable to water and oxygen
Long shelf-life
Visco-Elastic Coating Materials covered Visco-Elastic Tape,Visco-Elastic Mastic,PVC Outerwrap Tape,Polypropylene Anticorrosion Tape,High Temperature Visco Tape
Visco-Elastic Tape is a wraparound corrosion protective coating consisting of a modified and reinforced visco-elastic adhesive applied onto a polyethylene carrier film.
Visco-elastic can be used for the coating of pipes, coating of risers, coating of flanges, coating of manholes, coating of valves, coating of offshore risers and pillars, underwater coating of risers, coating of welded sockets, repair of all type of coatings, sealing of pipe and cable conduits, sealing of tank chimes, sealing of pipe casings.
| Executive Standard | ISO21809-3:2016 Petroleum and natural gas industries — External coatings for buried or submerged pipelines used in pipeline transportation systems — Part 3: Field joint coatings | |||
| echnical Index Property | Test Standard | Outer Wrap Tape (FJC 13A) | Heat Shrinkable Outer Wrap (FJC 13B) | |
| Visco Ealstic Body Adhesive Tape | ||||
| Max Operating Temperature | -- | ≤50℃ (FJC 13A-1) ≤70℃ (FJC 13A-2) ≤95℃ (FJC 13A-3) ≤120℃ (FJC 13A-4) | ≤50℃ (FJC 13B-1) ≤70℃ (FJC 13B-2) ≤95℃ (FJC 13B-3) ≤120℃ (FJC 13B-4) | |
| Environment Temperature Range | -- | -60℃~50℃ (FJC 13A-1) -60℃~70℃ (FJC 13A-2) -60℃~95℃ (FJC 13A-3) -60℃~120℃ (FJC 13A-4) | -60℃~50℃ (FJC 13B-1) -60℃~70℃ (FJC 13B-2) -60℃~95℃ (FJC 13B-3) -60℃~120℃ (FJC 13B-4) | |
| Minimum thickness, at 23℃, mm | ISO21809-3 Annex B | 1.85 or other | 1.85 or other | |
| Glass transition temperature, ℃ | ISO11357-2 | <-60 | <-60 | |
| Crystallization temperature, ℃ | ISO11357-3 | <-100 | <-100 | |
| Holiday detection at 5 kV/ mm + 5 kV, max. 25 kV | ISO21809-3 Annex C | No holiday | No holiday | |
| Drip resistance, at Tmax+20℃(minimum 80 °C) | ISO21809-3 Annex K | No dripping of compound | No dripping of compound | |
| Adhesion test of reinforced compound with respect to steel and to plant coating before and after thermal ageing and before and after hot-water immersion, both for 100 days
to steel, at 23℃, Coverage, N/mm, % to steel, at Tmax+20℃, Coverage, N/mm, %
to plant coating, at 23℃, Coverage, N/mm, % to plant coating, at Tmax+20℃, Coverage, N/mm, % | ISO21809-3 Annex H ISO21809-3 Annex I | Cohesive separation mode
0.08, >95 0.03, >95
0.07, >95 0.03, >95 | Cohesive separation mode
0.08, >95 0.03, >95
0.07, >95 0.03, >95 | |
| Adhesion test of compound without reinforcement with respect to steel and to plant coating before and after thermal ageing and before and after hot-water immersion, both for 100 days
to steel, at 23℃ to steel, at Tmax+20℃
to plant coating, at 23℃ to plant coating, at Tmax+20℃ | ISO21809-3 Annex I |
Leaved Leaved
Leaved Leaved |
Leaved Leaved
Leaved Leaved | |
| Lap shear resistance, Cohesive separation mode Coverage
at 23℃, N/mm2 at Tmax+20℃, N/mm2 | ISO21809-3 Annex I |
0.006, >95 0.003, >95 |
0.006, >95 0.003, >95 | |
| Specific electrical insulation resistance RS100, at 23℃, Ω⋅m2 RS100/RS70, at 23℃ | ISO21809-3 Annex E |
2.1*108 0.87 |
2.1*108 0.87 | |
| Complete Coating | ||||
| Impact resistance, at 23℃, J | ISO21809-3 Annex D | 16 | 16 | |
| Indentation resistance, Test pressure, 1,0N/mm2 at 23℃, mm at Tmax+20℃, mm | ISO21809-3 Annex E |
1.2 0.7 |
13.5 0.7 | |
| Cathodic disbondment resistance, at 28 days at 23℃, mm at Tmax+20℃, mm | |
0, no holiday 0, no holiday |
0, no holiday 0, no holiday | |
| Outer Material | ISO21809-3 Annex G ISO21809-3 Annex C | Outer wrap — Polymeric tape | Outer wrap — Heat-shrinkable material | |
| Peel strength of outer wrap layer to outer wrap layer at 23℃, N/mm at Tmax+20℃, N/mm | ISO21809-3 Annex L |
0.25 0.03 |
1.2 0.3 | |
| Peel strength to plant coating,Elastic modulus after thermal ageing at 23℃, N/mm at Tmax+20℃, N/mm | ISO21809-3 Annex H |
1.26 0.13 |
1.2 0.3 | |
| Peel strength (P′100/P′0) outer layer to outer layer after hot water immersion for 100 days
at Tmax, max. 95 °C./at 23℃ | ISO21809-3 Annex L ISO21809-3 Annex I |
0.88 |
0.88 | |
| Peel strength (P100/P0) to plant coating after hot water immersion for 100 days
at Tmax, max. 95 °C./at 23℃ | ISO21809-3 Annex H ISO21809-3 Annex I |
0.87 |
0.87 | |
| Elastic modulus (E100/E0) after thermal ageing for 100 days
at Tmax+20℃/at 23℃ | ISO527-2 |
0.87 |
0.87 | |
| Peel strength (P′100/P′0) outer wrap layer to outer wrap layer after thermal ageing for 100 days
at Tmax+20℃/at 23℃ | ISO21809-3 M |
0.57 |
0.57 | |
| Peel strength to plant coating after thermal ageing (P100/P0) for 100 days
at Tmax+20℃/at 23℃ | ISO21809-3 M |
0.82 |
0.82 | |
| Installation Instructions | 1. Surface treatment The surface rust of pipe body is removed by mechanical rust removal equipment (electric angle mill), and the derusting grade reaches ST2. After rust removal, the surface of the pipe body is dried by a heat blower. 2. Pipe body wrapped with viscoelastic anti-corrosion tape Wrap a layer of viscoelastic anti-corrosion tape around the pipe section which has finished surface treatment, and the lap length between the end and the original coating shall not be less than 50mm. The minimum lap length of the joint of anti-corrosion tape is 10 mm. When wrapping the viscoelastic anti-corrosion tape, it is unnecessary to maintain a large tension, and press the edge and overlapping part of the tape by hand. 3. Flange and other special-shaped parts wrapped with viscoelastic anti-corrosion tape For the anti-corrosion operation at the connection of valve flange, the connecting bolt can be filled with anti-corrosion paste and coated with viscoelastic anti-corrosion tape. 4. Wrapping outer protective tape The basic operation method is the same as that of viscoelastic anti-corrosion tape, but the tension shall be maintained when wrapping the outer protective tape. The overlapping amount of joint part is 50%. The two ends of the anticorrosive pipe section shall be exposed 1-2mm respectively, and the outer protective tape shall not be wrapped. 5. Quality inspection The quality requirements for installation of viscoelastic anti-corrosion tape and outer protective tape: the surface is flat, overlapping is even, and there is no bubble, wrinkle and damage. | |||
About Us
Related Products List
Contact Us
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Fill in more information so that we can get in touch with you faster
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Contact Now